• Class

        NC/ROL0

        J-STD-005C

      • Stencil

        > 8 hours

        hrs at 30-70% R/H @20-25ºC

      • Tack

        42-44

        Tack force g/cm

      • Print

        210-300

        Viscosity in Malcom mPA/s 10RPM @25ºC x10³

      • Dispense

        100-140

        Viscosity in Malcom mPA/s 10RPM @25ºC x10³

      Skip to product information
      1 of 1

      STIRRI®

      SKU:SP-SV2-020-062-3

      Mesh Type
      Packaging
      Regular price $16.32 USD
      Regular price $16.32 USD Sale price $16.32 USD
      Sale Sold out

      V2-062 Sn62Pb36Ag2 no-clean mid-temp low voiding leaded eutectic solder paste 2% Silver (ROL0)

      • Sn62Pb36Ag2 soldering paste for SMT assemblies conforming to space exploration and defense contractors specs. Small syringe container for repair/rework, prototyping. Liquidus/solidus point - 179ºC (Eutectic). Powder composition: 62% Tin, 36% Lead, 2% Silver. Made with MT-TF no-clean soldering tacky paste flux
      • High-quality leaded Sn/Pb solder powder made using virgin raw materials. Consistently shaped microscopic granules evenly suspended in a translucent body of rosin soldering tacky flux. Activates immediately, demonstrating professional industrial wetting on most PCB finishes, smooth dispensing, quick and efficient soldering/desoldering and effortless cleaning with IPA or Hot Air
      • STIRRI-MT solder paste can be applied as a BGA alternative or as a liquid solder for PCB repair and rework - delivers instant bridge-free reflow with Hot Air. Quick response to a solder iron. Essential for leaded rework/repair, solar exploration, unmanned flying devices and military tech
      • Clear residue is not corrosive can be left on PCB, removed with isopropanol, cleaned in ultrasonic or a vapor degreasers. Contains QC-Aid special optical tracer glowing in UV for immediate visual PCB contamination inspection - easy to detect using UV/blacklight light and easy to clean using Isopropanol or any industrial solvent cleaner - paste will glow in UV highlighting affected areas. QC-Aid - Everyone Can QC!
      • Factory-made in the USA using certified conflict-free solder powder traced back to original alloy smelters. 

      Suitability

      Solder Paste Viscosity

      Values in Malcom @ 10 RPM/25ºC x10³ mPa/s
      Printing: 210-300
      Dispensing: 100-140

      Stencil Life

      Hrs @ 30-45% RH and 20-25°C

      > 8 hours Hrs @ 45-75% RH and 20-25°C

      Printer Operation

      Print Speed: 25-100 mm/sec

      Squeegee Pressure: 70-250g/cm of blade

      Under Stencil Wipe: Once every 10-25 prints, or as necessary

      Some adjustments may be necessary depending on process requirements

      Stencil Cleaning

      No-clean solder paste that can be left on the board for many SMT assemblies. For applications requiring cleaning, the paste can be cleaned using commercial residue removers.

      Automated cleaning systems for both stencil and misprinted boards. Manual cleaning using isopropyl alcohol (IPA), co-solvents and/or ultrasonic scrubbers, vapor degreaser.

      Do you make this paste untraceable - without QCA?

      UV light is for optional for QC certification only - not required for operating the paste.

      However, this material is also available untraceable - without QC-Aid™, meaning no specific optical UV-tracer has been deployed. Contact us for the MPN (Manufacturing Part Number) without UV-tracer.

      Storage and Handling

      To obtain the maximum shelf life STIRRI Soldering Paste & Liquid Solder™ should be stored in a refrigerator between 3-8°C (37-46°F). Unopened solder paste stored at room temperature, 25°C (77°F). Syringes and cartridges should be stored in the refrigerator vertically, dispensing tip pointing down.

      Allow 4-8 hours for solder paste to reach optimal operating temperature of 20-25°C (68-77°F). To avoid condensation inside solder paste - keep solder paste container sealed while warming the solder paste to operating temperature, otherwise moisture may end up inside the container and contaminate solder paste!

      NEVER FREEZE SOLDER PASTE!

      Safety Notice

      This product is designed for professional consumers. Information contained herein is based on technical data that we believe to be reliable and is intended for use by persons having technical skill, at their own risk. Consumers should make their own tests to determine the suitability of each product for their particular process. Manufacturer or distributors will assume no liability for results obtained or damages incurred through the application of the data presented - try on a small non-critical surface first!

      View full details

      You are in good hands!

      Made in the USA to the applicable industry standards 100% customer satisfaction guaranteed!

      Liquid-proof the assembly with Nano-Coating - dries in less than 8 seconds

      STIRRI HydraCoat™ is a liquid repellent making PCB liquid proof, instantly improving assembly value!

      With an impressive droplet contact angle of over 113º, this nonconducting solution creates an invisible hydrophobic shield repelling weather, humidity, moisture - coated PCB continues to function even when fully submerged!

      Broadly suited for consumer devices, automotive circuits, urban and landscaping lightning, LED, medical or electronic devices, marine, boating and yachting industries.

      Dry to touch in less than 8 seconds, self cures in 24 hrs or 10 min in 60ºC chamber.

      STIRRI's Conformal nano-coating ensures end-customer satisfaction while virtually eliminating assembly claims due to environmental or consumer liquid damages.

      Shop Now